SabikStat-konNoryl_HMC202M resin adalahDATA ON BK1005 saja.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4.1 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4.1 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 7580 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 135 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6890 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 86 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 86 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 145 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7150 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 267 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 9 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 180 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 177 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 171 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 181 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 173 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 6.12E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 1.58E-04 | 1/°C | ASTM D 696 |
| CTE, 23°C sampai 150°C, aliran | 1.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.7E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 180 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 177 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.1 - 0.3 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/5,0 kgf | 7.6 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+04 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Diakui, Kelas Api 94V-1 (3) | 1.49 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:12/14/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 300 - 325 | °C |
| Suhu Nozzle | 300 - 325 | °C |
| Suhu depan - Zona 3 | 290 - 325 | °C |
| Tengah - Zona 2 Suhu | 275 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 315 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 30 - 70 | % |
| Sumber GMD, terakhir diperbarui:12/14/2001 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Noryl_HMC202M.pdf |
|