SabikStat-konNoryl_FMC3008A resinadalah 30% serat karbon/kaca/mineral yang diisi, statis dissipative, resin busa. UL94 V1 dinilai.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| busa - MEKANIS 6.4 mm Wt Pengurangan | 20 | % | - |
| Tekanan tarik, hasil, 6,35 mm | 48 | MPa | ASTM D 638 |
| Tekanan tarik, putus, 6,35 mm | 3.5 | % | ASTM D 638 |
| Tekanan lentur, hasil, 6,4 mm | 102 | MPa | ASTM D 790 |
| Flexural Modulus, 6,4 mm | 7790 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| BUMEN - Dampak 6.4 mm Wt Pengurangan | 20 | % | - |
| Izod Impact, tidak bertanda, 23°C, 6,4mm | 101 | J/m | ASTM D 4812 |
| Termal | Nilai | Satuan | Standar |
| BUMEN - PEMERINTAH 6.4mm Wt Pengurangan | 20 | % | - |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 116 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 108 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| busa - PHYSICAL 6.4mm Wt Pengurangan | 20 | % | - |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Gravitasi spesifik, cetakan busa | 1.02 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.15 - 0.25 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.15 - 0.35 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| busa - Listrik 6.4 mm Wt Pengurangan | 20 | % | - |
| Resistivitas Volume | 1.E+04 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+05 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| FOAM - Kelas Api Kepadatan Minimal | 1.15 | g/cm3 | - |
| UL diakui, 94V-0 Flame Class Rating (3) | 3.98 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui: 02/08/1993 | |||
| Parameter | ||
| Membentuk busa struktural | Nilai | Satuan |
| Agen Blowing, Sistem Fisik | Gas nitrogen | - |
| Agen Blowing, Sistem Kimia | FNC30X | - |
| Jangkauan konsentrasi (Agen Blowing) | 1 - 3 | % |
| Konsentrasi yang Disarankan (Agen Blowing) | 2 | % |
| Suhu pengeringan (resin) | 105 - 110 | °C |
| Waktu pengeringan (resin) | 2 - 4 | jam |
| Waktu pengeringan (resin, kumulatif) | 8 | jam |
| Suhu Peleburan | 270 - 300 | °C |
| Suhu Nozzle | 270 - 300 | °C |
| Suhu Depan | 270 - 300 | °C |
| Suhu Rata-rata | 270 - 290 | °C |
| Suhu Belakang | 260 - 280 | °C |
| Suhu Cetakan | 70 - 95 | °C |
| Sumber GMD, terakhir diperbarui: 02/08/1993 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Noryl_FMC3008A.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|