SabikStat-konDX92440resin adalahsenyawa yang didasarkan pada resin polikarbonat yang mengandung Flame Retardant, stainless steel.
bahan ini meliputi: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 57 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 49 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 4.3 | % | ASTM D 638 |
| Tekanan tarik, putus | 7.8 | % | ASTM D 638 |
| Tekanan Flexural | 99 | MPa | ASTM D 790 |
| Modulus Flexural | 2900 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1308 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 65 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 51 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.36 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.8 | % | ASTM D 955 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+04 - 1.E+05 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.65 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 275 - 305 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 280 - 295 | °C |
| Bagian belakang - Zona 1 Suhu | 265 - 275 | °C |
| Suhu Cetakan | 95 - 120 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
Untuk informasi lebih lanjut silahkan download lembar data | |
 | S-Plastics Stat-konDX92440.pdf |