SabikStat-konCycoloy_JK800 resinadalah 8% serat karbon diperkuatPC + ABS, dissipative elektrostatik ECO sesuai FR. Baik
stabilitas hidrolisis.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 7580 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 144 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6200 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.9 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 145 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6380 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 347 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 82 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 21 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 111 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 97 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 92 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 94 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.52E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.48E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 2.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 101 | °C | ISO 306 |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.25 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.1 - 0.2 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/2,16 kgf | 17 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+03 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+06 | Ohm | ASTM D 257 |
| Kerusakan statis, 5000V hingga <50V | 0.01 | < detik | FTMS101B |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.99 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 1.49 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui: 29/10/2002 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 80 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 230 - 275 | °C |
| Suhu Nozzle | 230 - 275 | °C |
| Suhu depan - Zona 3 | 225 - 275 | °C |
| Tengah - Zona 2 Suhu | 215 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 210 - 255 | °C |
| Suhu Cetakan | 50 - 70 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 30 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui: 29/10/2002 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon Cycoloy_JK800.pdf |
|
Dapatkan Kutipan Terbaru