SabikStat-konZE004 resinadalah senyawa berdasarkan resin POYPHENYLENE yang dimodifikasi yang mengandung Serat Karbon.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 80 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 104 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 0.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 24820 | MPa | ASTM D 638 |
| Tekanan Flexural | 179 | MPa | ASTM D 790 |
| Modulus Flexural | 24130 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 54 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 103 | MPa | ISO 527 |
| Tekanan tarik, putus | 0.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 14720 | MPa | ISO 527 |
| Tekanan Flexural | 151 | MPa | ISO 178 |
| Modulus Flexural | 12700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 299 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 17 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 139 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 137 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 4.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 3.7E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.17 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.4 - 0.6 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.3 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.53 | % | ISO 294 |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 300 - 305 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 290 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/24/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |