SabikUltem ATX153Rresin adalah30% serat kaca yang diisi, campuran Polyetherimide aliran tinggi dengan pelepasan cetakan internal.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 144 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 144 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.5 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9690 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 203 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 8610 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 143 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 143 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9680 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 218 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 8720 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 854 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 107 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 15 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 47 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 49 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 193 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 191 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 182 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 193 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 185 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 1.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 5.8E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 150°C, aliran | 1.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.8E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 190 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 192 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 180 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 169 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.47 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.2 - 0.4 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 30 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.47 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 28 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.1E+16 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | 2.3E+16 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 23 | kV/mm | IEC 60243-1 |
| Faktor Dissipasi, 50/60 Hz | 0.0037 | - | IEC 60250 |
| Faktor Dissipasi, 1 kHz | 0.0035 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.0096 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 125 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 125 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:04/28/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 340 - 360 | °C |
| Suhu Nozzle | 330 - 355 | °C |
| Suhu depan - Zona 3 | 340 - 360 | °C |
| Tengah - Zona 2 Suhu | 325 - 350 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 340 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/28/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem ATX153R.pdf |
|