SabikStat-konDX09301Cresin adalahLow Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound cocok untuk aplikasi Semiconductor and Hard Disk Drive (HDD).Fitur tambahan dari bahan ini meliputi:Sistem Komposisi Bersih.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 64 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 5.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 15 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2670 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 101 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2600 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 66 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 54 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.1 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 12 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 99 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2560 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 2160 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 52 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 8 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 200 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 138 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.224 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam (5) | 0.5 - 0.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 0.5 - 0.7 | % | ASTM D 955 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+05 - 1.E+08 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+05 - 1.E+08 | Ohm | ASTM D 257 |
| Kerusakan statis, 5000V hingga <50V | 0.1 | < detik | FTMS101B |
| Sumber GMD, terakhir diperbarui:2010/05/21 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2010/05/21 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon DX09301C.pdf |
|