SabikStat-konDX05499resin adalahsenyawa berbasis resin polikarbonat yang mengandung Carbon Powder, Flame Retardant.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 67 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 60 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 4.6 | % | ASTM D 638 |
| Tekanan tarik, putus | 8.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2750 | MPa | ASTM D 638 |
| Tekanan Flexural | 101 | MPa | ASTM D 790 |
| Modulus Flexural | 3230 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 64 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 53 | MPa | ISO 527 |
| Tekanan tarik, hasil | 4.3 | % | ISO 527 |
| Tekanan tarik, putus | 12.6 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2800 | MPa | ISO 527 |
| Tekanan Flexural | 108 | MPa | ISO 178 |
| Modulus Flexural | 3100 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 2354 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 96 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 25 | J | ASTM D 3763 |
| Dampak Multiaxial | 34 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 137 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 120 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.34 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.11 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.6 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.7 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.64 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.66 | % | ISO 294 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.19 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+05 - 1.E+09 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 0.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon DX05499.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|