SabikStat-konDX04490resin adalahsenyawa berbasis resin polikarbonat yang mengandung Carbon Powder.
termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 60 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 53 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 4.2 | % | ASTM D 638 |
| Tekanan tarik, putus | 16.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2980 | MPa | ASTM D 638 |
| Tekanan Flexural | 89 | MPa | ASTM D 790 |
| Modulus Flexural | 2710 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 61 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 54 | MPa | ISO 527 |
| Tekanan tarik, hasil | 4.5 | % | ISO 527 |
| Tekanan tarik, putus | 8.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2710 | MPa | ISO 527 |
| Tekanan Flexural | 75 | MPa | ISO 178 |
| Modulus Flexural | 2510 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 2342 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 48 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 4 | J | ASTM D 3763 |
| Dampak Multiaxial | 9 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 167 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 6.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.94E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 6.35E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.08E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.23 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.42 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.5 | % | ISO 294 |
| Kepadatan | 1.23 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | - 3.E+00 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | - 2.E+00 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:03/20/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:03/20/2006 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon DX04490.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|