SabikStat-konDX03633Cresin adalahsenyawa berbasis resin polikarbonat yang mengandung Carbon Powder.
termasuk: Clean Compounding System.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 87 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 2.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 6180 | MPa | ASTM D 638 |
| Tekanan Flexural | 143 | MPa | ASTM D 790 |
| Modulus Flexural | 5570 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 373 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.27 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.38 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.46 | % | ASTM D 955 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+04 - 1.E+00 | Ohm-cm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon DX03633C.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|