SabikUltem LTX931Aresin adalahBerbasis daur ulang pasca-industri, 30% isi serat kaca, campuran Polyetherimide aliran tinggi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 115 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 115 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 9200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 190 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 8300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 150°C, aliran | 1.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.8E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 188 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 195 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 184 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.52 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.4 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.25 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 19 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/28/2004 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 340 - 360 | °C |
| Suhu Nozzle | 330 - 355 | °C |
| Suhu depan - Zona 3 | 340 - 360 | °C |
| Tengah - Zona 2 Suhu | 325 - 350 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 340 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/28/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem LTX931A.pdf |
|