SabikUltem HU2210resin adalah20% Serat kaca diisi, aliran ditingkatkan Polyetherimide (Tg 217C). ECO sesuai. Untuk perangkat medis dan aplikasi farmasi.biocompatible (ISO 10993 atau USP Kelas VI), sesuai dengan kontak makanan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 139 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 140 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 4 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6890 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 227 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6890 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 140 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 140 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6800 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 210 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 475 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 64 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 13 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 226 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 211 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 218 | °C | ISO 306 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.42 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm (5) | 0.3 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 8.4 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.42 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.55 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:2010/01/04 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:2010/01/04 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem HU2210.pdf |
|