SabikStat-konDE002resin adalahPolycarbonate yang mengandung Serat Karbon
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 97 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 7.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11140 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 159 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 7460 | MPa | ASTM D 790 |
| Tekanan tarik, pecah, 5 mm/menit | 97 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 7.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10340 | MPa | ISO 527 |
| Tekanan Flexural | 149 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7440 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 9 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 1 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 32 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 146 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 141 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 2.6E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 5.8E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 145 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.29 | - | ASTM D 792 |
| Kepadatan | 1.29 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.08 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.4 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.4 - 0.6 | % | ASTM D 955 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 4.E+00 - 6.E+00 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 3.E+00 - 5.E+00 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:09/11/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/11/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon DE002.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|