SabikUltem EXUM0025resin adalah30% Diisi dengan kaca bubuk, Polyetherimide aliran tinggi (Tg 217C) dengan pelepasan cetakan internal dan peningkatan elektroplatability.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 105 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 105 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 8480 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 7260 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 75 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 5 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 145 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5500 | MPa | ISO 178 |
| Kekerasan, H358/30 | 155 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 430 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 59 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 25 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 25 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 216 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 208 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 206 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 209 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 205 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 3.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 3.5E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.32 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 150°C, aliran | 3.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 3.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 213 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 195 | °C | ISO 75/Ae |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 204 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 193 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.48 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 13 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.48 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 14 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 4 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 4 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Sumber GMD, terakhir diperbarui:10/28/2003 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 360 - 400 | °C |
| Suhu Nozzle | 360 - 400 | °C |
| Suhu depan - Zona 3 | 370 - 410 | °C |
| Tengah - Zona 2 Suhu | 360 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 340 - 380 | °C |
| Suhu Hopper | 80 - 100 | °C |
| Suhu Cetakan | 140 - 180 | °C |
| Sumber GMD, terakhir diperbarui:10/28/2003 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |