SabikUltem EXSM0010resin adalahFR SILTEM resin dengan peningkatan nyala api, asap & toksisitas sesuai dengan ASTM E162, ASTM E662 dan SMP800C.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 36 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 34 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 12 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 30 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1350 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 55 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1250 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 300 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 100 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 77 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:2010/04/08 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 320 | °C |
| Suhu Nozzle | 310 - 320 | °C |
| Suhu depan - Zona 3 | 310 - 320 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 310 - 320 | °C |
| Suhu Cetakan | 105 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:2010/04/08 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem EXSM0010.pdf |
|