SabikStat-konDD0009resin adalahsebuah senyawa berbasis resin polikarbonat yang mengandung Flame Retardant, Carbon Powder.
bahan ini meliputi: Konduktif, tahan api.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 61 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 53 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 1.2 | % | ASTM D 638 |
| Tekanan tarik, putus | 5.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2820 | MPa | ASTM D 638 |
| Tekanan Flexural | 108 | MPa | ASTM D 790 |
| Modulus Flexural | 2820 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 62 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 57 | MPa | ISO 527 |
| Tekanan tarik, hasil | 4.1 | % | ISO 527 |
| Tekanan tarik, putus | 7.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2810 | MPa | ISO 527 |
| Tekanan Flexural | 102 | MPa | ISO 178 |
| Modulus Flexural | 2880 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1556 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 68 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 10 | J | ASTM D 3763 |
| Dampak Multiaxial | 5 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 70 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 141 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.36E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.67E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.36E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.67E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 139 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.32 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.18 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.8 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.7 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.75 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.72 | % | ISO 294 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.27 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 4.E+00 - 6.E+00 | Ohm | ASTM D 257 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.7 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:09/30/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 255 - 290 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 255 - 265 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 260 | °C |
| Suhu Cetakan | 40 - 65 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/30/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |