SabikStat-konCX99000resin adalahKomposisi berbasis Polystyrene yang mengandung Carbon Powder.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 24 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 23 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.8 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1700 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 41 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 90 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 75 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran | 0.8 | % | Metode S-Plastics |
| Kepadatan | 1.1 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+04 - 1.E+06 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:04/16/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 250 | °C |
| Suhu depan - Zona 3 | 265 - 275 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 40 - 65 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:04/16/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon CX99000.pdf |
|