SabikUltem 2100Nresin adalah10% Isi serat kaca, aliran standar Polyetherimide (Tg 217C).
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 114 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 115 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4680 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 199 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 5170 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 114 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 480 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 459 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 223 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 210 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 208 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 3.24E-05 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.34 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.21 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 1.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 7 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 27.5 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 1 kHz | 3.5 | - | ASTM D 150 |
| Faktor Dissipasi, 1 kHz | 0.0014 | - | ASTM D 150 |
| Faktor Dissipasi, 2450 MHz | 0.0046 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem 2100N.pdf |
|