SabikVertonWV00A resinadalah senyawa yang didasarkan pada resin Polybutylene Terephalate yang mengandung Long Glass.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 154 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 20240 | MPa | ASTM D 638 |
| Tekanan Flexural | 233 | MPa | ASTM D 790 |
| Modulus Flexural | 14400 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 163 | MPa | ISO 527 |
| Tekanan tarik, putus | 1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 19770 | MPa | ISO 527 |
| Tekanan Flexural | 235 | MPa | ISO 178 |
| Modulus Flexural | 15670 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 831 | J/m | ASTM D 4812 |
| Energi Dampak Instrumen @ puncak, 23°C | 12 | J | ASTM D 3763 |
| Dampak Multiaxial | 11 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 59 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 43 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 223 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.85E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.14E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.85E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 4.14E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 225 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.7 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.1 - 0.3 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.4 - 0.7 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.08 - 0.29 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.43 - 0.72 | % | ISO 294 |
| Kepadatan | 1.7 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/03/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 250 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 260 | °C |
| Tengah - Zona 2 Suhu | 240 - 250 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Cetakan | 65 - 120 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 70 | rpm |
| Sumber GMD, terakhir diperbarui:10/03/2004 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton WV00A.pdf |
|