SabikStat-kon9X06519resin adalahsenyawa yang didasarkan pada resin Cyclic Olefinic Copolymer yang mengandung Serat Karbon.
Bahan termasuk: Sistem Komposisi Bersih.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 74 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 0.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 16040 | MPa | ASTM D 638 |
| Tekanan Flexural | 158 | MPa | ASTM D 790 |
| Modulus Flexural | 16680 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 122 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 150 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.8E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.26E-05 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.17 | g/cm3 | ASTM D 792 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+01 - 1.E+05 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:02/03/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 260 - 315 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 275 - 290 | °C |
| Bagian belakang - Zona 1 Suhu | 255 - 265 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:02/03/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon 9X06519.pdf |
|