SabikVertonWV007XXP resinadalah senyawa yang didasarkan pada resin Polybutylene Terephalate yang mengandung Long Glass.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 146 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 14000 | MPa | ASTM D 638 |
| Tekanan Flexural | 213 | MPa | ASTM D 790 |
| Modulus Flexural | 10390 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 141 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 13440 | MPa | ISO 527 |
| Tekanan Flexural | 209 | MPa | ISO 178 |
| Modulus Flexural | 11230 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 705 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 278 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 11 | J | ASTM D 3763 |
| Dampak Multiaxial | 9 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 37 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 27 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 222 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.61E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 3.62E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 231 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.59 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.2 - 0.5 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 - 0.9 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.21 - 0.55 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.55 - 0.93 | % | ISO 294 |
| Kepadatan | 1.59 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/03/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 250 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 260 | °C |
| Tengah - Zona 2 Suhu | 240 - 250 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Cetakan | 65 - 120 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 70 | rpm |
| Sumber GMD, terakhir diperbarui:10/03/2004 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton WV007XXP.pdf |
|