SabikStat-kon9X04323resin adalahsenyawa yang didasarkan pada resin Noryl GTX,Fitur tambahan dari bahan ini termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2760 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 99 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2400 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 59 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 58 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 3.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2780 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2590 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 180 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 168 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 2.4E-05 | 1/°C | ASTM E 831 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 181 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 163 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.11 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.93 - 1.24 | % | ASTM D 955 |
| Kepadatan | 1.11 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | 1.E+02 - 1.E+04 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:08/05/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 300 - 305 | °C |
| Suhu depan - Zona 3 | 300 - 310 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 275 - 290 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:08/05/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |