SabikVertonWV007S resinadalah senyawa yang didasarkan pada resin Polybutylene Terephalate yang mengandung Long Glass Fiber.
Bahan termasuk: Heat Stabilized.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 145 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 14000 | MPa | ASTM D 638 |
| Tekanan Flexural | 213 | MPa | ASTM D 790 |
| Modulus Flexural | 10390 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 141 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 13440 | MPa | ISO 527 |
| Tekanan Flexural | 210 | MPa | ISO 178 |
| Modulus Flexural | 11240 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 694 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 277 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 11 | J | ASTM D 3763 |
| Dampak Multiaxial | 9 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 27 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 222 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.48E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 3.62E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 231 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.59 | g/cm3 | ASTM D 792 |
| Sumber GMD, terakhir diperbarui:02/27/2007 | |||