SabikStat-kon9X02785resin adalahsenyawa berbasis resin polikarbonat yang mengandung Filler Proprietary (s).
termasuk: Konduktif listrik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 64 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2890 | MPa | ASTM D 638 |
| Tekanan Flexural | 103 | MPa | ASTM D 790 |
| Modulus Flexural | 2890 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 66 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 102 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.26 | g/cm3 | ASTM D 792 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+02 - 1.E+07 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+02 - 1.E+07 | Ohm | ASTM D 257 |
| Sumber GMD, terakhir diperbarui:10/01/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 305 - 325 | °C |
| Suhu depan - Zona 3 | 320 - 330 | °C |
| Tengah - Zona 2 Suhu | 310 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C |
| Suhu Cetakan | 80 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/01/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Stat-kon 9X02785.pdf |
|