SabikVertonUX06451resinadalah senyawa yang didasarkan pada resin Polyphthalamide yang mengandung Long Glass Fiber.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 274 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 19300 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 275 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.7 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 19000 | MPa | ISO 527 |
| Tekanan Flexural | 375 | MPa | ISO 178 |
| Modulus Flexural | 17400 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1495 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 411 | J/m | ASTM D 256 |
| Dampak Multiaxial | 14 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 75 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, aliran | 2.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 3.2E-05 | 1/°C | ISO 11359-2 |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.63 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.3 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.06 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.2 | % | ISO 294 |
| Kepadatan | 1.63 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:01/02/2007 | |||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |