SabikVertonUX03320 resinadalah senyawa yang didasarkan pada resin Polyphthalamide yang mengandung Long Glass.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 220 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 18200 | MPa | ASTM D 638 |
| Tekanan Flexural | 300 | MPa | ASTM D 790 |
| Modulus Flexural | 18000 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 245 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 200 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.5 | % | ISO 527 |
| Tekanan tarik, putus | 1.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 20360 | MPa | ISO 527 |
| Modulus tarik, 1 mm/menit | 20300 | MPa | ISO 527 |
| Tekanan Flexural | 360 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 360 | MPa | ISO 178 |
| Modulus Flexural | 17700 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 17700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 800 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 300 | J/m | ASTM D 256 |
| Dampak Multiaxial | 19 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 15 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 70 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 38 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 +23°C | 38 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 260 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 2.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 2.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 276 | °C | ISO 75/Af |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 275 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.63 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.05 - 0.1 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.08 - 0.2 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.06 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.15 | % | ISO 294 |
| Aliran spiral (1mm) | 30 | cm | Metode S-Plastics |
| Aliran spiral (3mm) | 70 | cm | Metode S-Plastics |
| Kepadatan | 1.63 | g/cm3 | ISO 1183 |
| Kepadatan | 1.63 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.3 | % | ISO 62 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:02/08/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 - 150 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 | % |
| Suhu Peleburan | 315 - 330 | °C |
| Suhu depan - Zona 3 | 330 - 345 | °C |
| Tengah - Zona 2 Suhu | 320 - 330 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 325 | °C |
| Suhu Cetakan | 140 - 165 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:02/08/2008 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton UX03320.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|