SabikVertonUV00AS resinadalah senyawa yang didasarkan pada resin Polyphthalamide yang mengandung Long Glass Fiber.
Termasuk: Stabilisasi panas.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 257 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 257 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 1.8 | % | ASTM D 638 |
| Tekanan tarik, putus | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 19300 | MPa | ASTM D 638 |
| Tekanan Flexural | 386 | MPa | ASTM D 790 |
| Modulus Flexural | 17230 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 222 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 222 | MPa | ISO 527 |
| Tekanan tarik, hasil | 1.4 | % | ISO 527 |
| Tekanan tarik, putus | 1.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 19220 | MPa | ISO 527 |
| Tekanan Flexural | 393 | MPa | ISO 178 |
| Modulus Flexural | 17000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1228 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 267 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 9 | J | ASTM D 3763 |
| Dampak Multiaxial | 7 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 78 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 41 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 291 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 266 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.06E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.44E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 3.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 296 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 272 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.67 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.2 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.2 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.5 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.2 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.48 | % | ISO 294 |
| Kepadatan | 1.66 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:06/13/2007 | |||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton UV00AS.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|