SabikVertonRV00AES resinadalah senyawa yang didasarkan pada resin Nylon 66 yang mengandung Long Glass.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 254 | MPa | ASTM D 638 |
| Tekanan tarik, putus | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 17510 | MPa | ASTM D 638 |
| Tekanan Flexural | 374 | MPa | ASTM D 790 |
| Modulus Flexural | 14160 | MPa | ASTM D 790 |
| Tekanan tegangan, istirahat | 256 | MPa | ISO 527 |
| Tekanan tarik, putus | 1.9 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 18380 | MPa | ISO 527 |
| Tekanan Flexural | 370 | MPa | ISO 178 |
| Modulus Flexural | 15550 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 384 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 15 | J | ASTM D 3763 |
| Dampak Multiaxial | 15 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 89 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 38 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 241 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.85E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.73E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.86E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 6.73E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 253 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.58 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.18 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.22 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.18 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.22 | % | ISO 294 |
| Kepadatan | 1.58 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 290 - 305 | °C |
| Suhu depan - Zona 3 | 290 - 300 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 295 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |