SabikVertonRV008ESV_GY7E072 resin adalahData awal untuk 40% serat kaca panjang yang diisi, warna tunggal pellet abu-abu, PA66
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 184 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 182 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.1 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11560 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 273 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 11300 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 195 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 195 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10440 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 276 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 10190 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1080 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 246 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 223 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 7 | J | ASTM D 3763 |
| Energi Total Dampak Instrumen, 23°C | 16 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 71 | kJ/m2 | ISO 180/1U |
| Izod Impact, tidak dicat 80*10*4 -40°C | 69 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 27 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 259 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 255 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 2.32E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C sampai 30°C, xflow | 5.83E-05 | 1/°C | ASTM E 831 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 256 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.485 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.93 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.23 - 0.43 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.9 - 1.1 | % | ASTM D 955 |
| Kepadatan | 1.48 | g/cm3 | ISO 1183 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.65 | % | ISO 62 |
| Sumber GMD, terakhir diperbarui:10/30/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 290 - 305 | °C |
| Suhu depan - Zona 3 | 290 - 300 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 295 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/30/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton RV008ESV_GY7E072.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|