SabikVertonPX91200 resinadalah senyawa berbasis resin Nylon 6 yang mengandung Long Glass, Lubricants.
termasuk: High Impact.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tegangan, istirahat | 181 | MPa | ISO 527 |
| Tekanan tarik, putus | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 12100 | MPa | ISO 527 |
| Tekanan Flexural | 250 | MPa | ISO 178 |
| Modulus Flexural | 10290 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 68 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 25 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 225 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 222 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.49 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:10/02/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.15 - 0.25 | % |
| Suhu Peleburan | 290 - 305 | °C |
| Suhu depan - Zona 3 | 290 - 300 | °C |
| Tengah - Zona 2 Suhu | 290 - 300 | °C |
| Bagian belakang - Zona 1 Suhu | 280 - 295 | °C |
| Suhu Cetakan | 95 - 110 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:10/02/2004 | ||
)