SabikVertonMV005SX0 resinadalah senyawa yang didasarkan pada resin PP yang mengandung Long Glass Fiber.
Panas stabil.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 104 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 7000 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 149 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Dampak Multiaxial | 4 | J | ISO 6603 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 14 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 163 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 158 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur, aliran, 24 jam | 0.5 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.81 | % | ISO 294 |
| Kepadatan | 1.1 | g/cm3 | ISO 1183 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Pengolahan | ||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 | °C |
| Waktu Pengeringan | 4 | jam |
| Suhu Peleburan | 220 - 250 | °C |
| Suhu depan - Zona 3 | 250 - 260 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Cetakan | 40 - 65 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:09/15/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Verton MV005SX0.pdf |
|
Dapatkan Kutipan Terbaru