SabikCycolacMG29resin adalahABS bertekanan tinggi, ketahanan suhu rendah, high gloss.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 38 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 26 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1990 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 64 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2060 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 453 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 28 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 98 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 96 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 81 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.54E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.36E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.04 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 230°C/3,8 kgf | 1.2 | g/10 menit | ASTM D 1238 |
| Viskositas peleburan, 240°C, 1000 detik-1 | 2800 | bergairah | ASTM D 3825 |
| Tingkat Aliran Peleburan, 220°C/10,0 kg | 10 | g/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 0 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 0 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.52 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:10/30/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 95 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.01 | % |
| Suhu Peleburan | 230 - 275 | °C |
| Suhu Nozzle | 230 - 275 | °C |
| Suhu depan - Zona 3 | 225 - 240 | °C |
| Tengah - Zona 2 Suhu | 210 - 220 | °C |
| Bagian belakang - Zona 1 Suhu | 190 - 200 | °C |
| Suhu Cetakan | 50 - 65 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Menembak untuk ukuran silinder | 50 - 70 | % |
| Kedalaman ventilasi | 0.038 - 0.051 | mm |
| Sumber GMD, terakhir diperbarui:10/30/2001 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Cycolac MG29.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|