SabikCycolacHXSresin adalahABS, aliran tinggi, kelas ekstrusi lembaran dengan dampak sedang.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 41 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 33 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2060 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 68 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2270 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 411 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 144 | J/m | ASTM D 256 |
| Jatuh Dart Imp, 23°C 3,2 mm extr sheet | 44 | J | Metode S-Plastics |
| Jatuh Dart Imp, -40°C 3,2 mm extr sheet | 16 | J | Metode S-Plastics |
| Energi Total Dampak Instrumen, 23°C | 45 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 105 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 90 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 81 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.04 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 230°C/3,8 kgf | 1.2 | g/10 menit | ASTM D 1238 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:06/17/1998 | |||
| • Merekomendasikan pengaturan suhu awal yang lebih rendah untuk menghindari degradasi material / gantung di die. | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 95 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0 - 0.02 | % |
| Suhu Peleburan | 215 - 260 | °C |
| Barel - Zona 1 Suhu | 170 - 200 | °C |
| Barel - Zona 2 Suhu | 180 - 220 | °C |
| Barel - Zona 3 Suhu | 190 - 225 | °C |
| Barel - Zona 4 Suhu | 200 - 240 | °C |
| Suhu adaptor | 205 - 250 | °C |
| Suhu mati | 205 - 250 | °C |
| Temperature Roll Stack - Atas | 90 - 95 | °C |
| Temperature Roll Stack - Pertengahan | 95 - 105 | °C |
| Roll Stack Temp - Bagian bawah | 100 - 105 | °C |
| Sumber GMD, terakhir diperbarui:06/17/1998 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Cycolac HXS.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|