SabikCycolacHXPresin adalahDATA PERTAMA. kelas ekstrusi, aliran tinggi, dampak sedang. proses yang sangat baik / estetika lembaran. aplikasi dapur dan kamar mandi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 43 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 33 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 23 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2370 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 77 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2480 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 106 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 363 | J/m | ASTM D 256 |
| Dampak panah jatuh (D 3029), 23°C | 42 | J | ASTM D 3029 |
| Energi Total Dampak Instrumen, 23°C | 47 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 107 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 95 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 82 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 93 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.04 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 5.2 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Glossy, tidak bertekstur, 60 deg (lampu) | 96 | - | ASTM D 523 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.52 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:01/15/1998 | |||
| • Merekomendasikan pengaturan suhu awal yang lebih rendah untuk menghindari degradasi material / gantung di die. | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 95 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0 - 0.02 | % |
| Suhu Peleburan | 215 - 260 | °C |
| Barel - Zona 1 Suhu | 170 - 200 | °C |
| Barel - Zona 2 Suhu | 180 - 220 | °C |
| Barel - Zona 3 Suhu | 190 - 225 | °C |
| Barel - Zona 4 Suhu | 200 - 240 | °C |
| Suhu adaptor | 205 - 250 | °C |
| Suhu mati | 205 - 250 | °C |
| Temperature Roll Stack - Atas | 90 - 95 | °C |
| Temperature Roll Stack - Pertengahan | 95 - 105 | °C |
| Roll Stack Temp - Bagian bawah | 100 - 105 | °C |
| Sumber GMD, terakhir diperbarui:01/15/1998 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Cycolac HXP.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|