SabikCycolacGX3800resin adalahABS dampak tinggi untuk ekstrusi lembaran dan aplikasi cetakan.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 39 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 30 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3.1 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 31.6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2080 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 66 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2160 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 432 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 299 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 50 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 106 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 93 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 80 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.01E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.03 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.8 | % | Metode S-Plastics |
| Viskositas peleburan, 240°C, 100 detik-1 | 14000 | bergairah | ASTM D 3825 |
| Tingkat Volume Peleburan, MVR pada 220°C/10,0 kg | 4 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/18/2002 | |||
| • Merekomendasikan pengaturan suhu awal yang lebih rendah untuk menghindari degradasi material / gantung di die. | ||
| • Menjaga suhu leleh dalam kisaran pengolahan. | ||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 4 - 5 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 00.02 - 0.04 | % |
| Kandungan Kelembaban Minimal | 0.04 | % |
| Suhu Peleburan (Parison) | 215 - 230 | °C |
| Barel - Zona 1 Suhu | 205 - 225 | °C |
| Barel - Zona 2 Suhu | 205 - 225 | °C |
| Barel - Zona 3 Suhu | 205 - 225 | °C |
| Barel - Zona 4 Suhu | 205 - 225 | °C |
| Adaptor - Zona 5 Suhu | 210 - 230 | °C |
| Kepala - Zona 6 - Suhu puncak | 215 - 230 | °C |
| Kepala - Zona 7 - Suhu bawah | 215 - 230 | °C |
| Kecepatan sekrup | 20 - 60 | rpm |
| Suhu zona pakan ekstruder | 60 - 75 | °C |
| Suhu Cetakan | 40 - 80 | °C |
| Suhu mati | 215 - 235 | °C |
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 95 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0 - 0.02 | % |
| Suhu Peleburan | 215 - 260 | °C |
| Barel - Zona 1 Suhu | 170 - 200 | °C |
| Barel - Zona 2 Suhu | 180 - 220 | °C |
| Barel - Zona 3 Suhu | 190 - 225 | °C |
| Barel - Zona 4 Suhu | 200 - 240 | °C |
| Suhu adaptor | 205 - 250 | °C |
| Suhu mati | 205 - 250 | °C |
| Temperature Roll Stack - Atas | 90 - 95 | °C |
| Temperature Roll Stack - Pertengahan | 95 - 105 | °C |
| Roll Stack Temp - Bagian bawah | 100 - 105 | °C |
| Sumber GMD, terakhir diperbarui:04/18/2002 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|