SabikCycolacFXS680SK resin adalahABS bening dengan VisualFx Sparkle Metallic
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 39 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 29 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 35 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2130 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 65 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2180 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 38 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 28 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 29 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2120 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 62 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2170 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 58 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 40 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 14 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 87 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 72 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.6E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.6E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.6E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.6E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 87 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 90 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 73 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.1 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 1.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.1 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.4 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:01/12/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 70 - 75 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.01 | % |
| Suhu Peleburan | 205 - 245 | °C |
| Suhu Nozzle | 205 - 245 | °C |
| Suhu depan - Zona 3 | 215 - 240 | °C |
| Tengah - Zona 2 Suhu | 205 - 225 | °C |
| Bagian belakang - Zona 1 Suhu | 195 - 215 | °C |
| Suhu Cetakan | 50 - 70 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Menembak untuk ukuran silinder | 50 - 70 | % |
| Kedalaman ventilasi | 0.038 - 0.051 | mm |
| Sumber GMD, terakhir diperbarui:01/12/2006 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|