SabikCycolacDL100 resin adalahIa panas tinggi, dampak tinggi, campuran ABS / PC emisi rendah.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 46 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 60 | % | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 10 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 69 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2250 | MPa | ISO 178 |
| Kekerasan, H358/30 | 91 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 111 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 35 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 34 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 9.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 9.8E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 101 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 104 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 104 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 84 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 60 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 60 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.7 | % | Metode S-Plastics |
| Kepadatan | 1.08 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) ((4) | 1.5 | mm | UL 94 oleh GE |
| UL Compliant, 94HB Flame Class Rating 2nd value (3) ((4) | 3 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:08/10/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.1 | % |
| Suhu Peleburan | 250 - 280 | °C |
| Suhu Nozzle | 245 - 275 | °C |
| Suhu depan - Zona 3 | 250 - 280 | °C |
| Tengah - Zona 2 Suhu | 250 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 40 - 80 | °C |
| Sumber GMD, terakhir diperbarui:08/10/1999 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Cycolac DL100.pdf |
|