S-Plastics ValoxENH8560resin adalah Non-Brominated & Non-Chlorinated Flame Retardant, 30% campuran PBT/PET diperkuat serat kaca
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 10000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 25 | kJ/m2 | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, aliran | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 180 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 190 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.6 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.3 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 25 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Faktor Dissipasi, 1 MHz | 0.0128 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 400 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 1,0 mm | 750 | °C | IEC 60695-2-13 |
| Suhu pembakaran kawat bercahaya, 2,0 mm | 775 | °C | IEC 60695-2-13 |
| Suhu pembakaran kawat bercahaya, 3,0 mm | 825 | °C | IEC 60695-2-13 |
| Sumber GMD, terakhir diperbarui:2010/06/17 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 285 | °C |
| Suhu Nozzle | 265 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 255 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 260 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 60 - 110 | °C |
| Sumber GMD, terakhir diperbarui:2010/06/17 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |