S-Plastics ValoxENH4550resin adalah 25% GF diperkuat, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 115 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 115 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 11000 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 157 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9370 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 115 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 115 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10400 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9350 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 48 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 42 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 6 | J | ASTM D 3763 |
| Izod Dampak, tidak bergaris 80*10*3 +23°C | 38 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 34 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 205 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 205 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 2.2E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 7.7E+01 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 2.2E+01 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.1E+01 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pergi | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 205 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 205 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.52 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.9 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 24 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.52 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.25 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 18 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan | 300 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 0.75 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 0,8 mm | 775 | °C | IEC 60695-2-13 |
| Sumber GMD, terakhir diperbarui:12/01/2008 | |||
| (1) Hanya nilai-nilai tipikal. variasi dalam toleransi normal mungkin untuk berbagai warna. semua nilai diukur setelah setidaknya 48 jam Semua sifat, kecuali volume leleh dan aliran leleh diukur pada mesin injeksi Semua sampel yang diuji menurut standar uji ISO disiapkan sesuai dengan ISO 294. |
|||
| (2) Hanya data tipikal untuk tujuan seleksi. | |||
| (3) Klasifikasi ini tidak dimaksudkan untuk mencerminkan bahaya yang ditimbulkan oleh bahan ini atau bahan lain dalam kondisi kebakaran yang sebenarnya. | |||
| (4) Pengukuran internal menurut standar UL. |
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Valox ENH4550.pdf |
|