S-Plastics Lubricomp EX07305resin adalah
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 157 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 8620 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 202 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 201 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 6420 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 156 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8540 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/menit | 7210 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 329 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 67 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 25 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 204 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.41E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.07E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 206 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.506 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran | 0.4 | % | Metode S-Plastics |
| Penyusutan jamur, aliran | 0.52 | % | Metode S-Plastics |
| Pakai faktor pencuci | 15 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.52 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.51 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 7.6E+16 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 2.E+13 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 31.4 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 kHz | 3.3 | - | ASTM D 150 |
| Faktor Dissipasi, 100 kHz | 0.0031 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:07/03/2008 | |||
Pengolahan
| Parameter | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 150 | °C | |
| Waktu Pengeringan | 4 - 6 | jam | |
| Waktu pengeringan (kumulatif) | 24 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 350 - 400 | °C | |
| Suhu Nozzle | 345 - 400 | °C | |
| Suhu depan - Zona 3 | 345 - 400 | °C | |
| Tengah - Zona 2 Suhu | 340 - 400 | °C | |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C | |
| Suhu Cetakan | 135 - 165 | °C | |
| Tekanan Belakang | 0.3 - 0.7 | MPa | |
| Kecepatan sekrup | 40 - 70 | rpm | |
| Menembak untuk ukuran silinder | 40 - 60 | % | |
| Kedalaman ventilasi | 0.025 - 0.076 | mm | |
| Sumber GMD, terakhir diperbarui:07/03/2008 | |||
Dalam beberapa tahun terakhir, kami telah mengembangkan pasar domestik dan secara aktif mengeksplorasi pasar luar negeri.Hingga saat ini, kami telah menyediakan produk dan layanan berkualitas tinggi untuk lebih dari 1.000 pelanggan di berbagai industri, termasuk: elektronik dan peralatan listrik, medis, makanan,elektronik otomotif, komunikasi optoelektronik, energi fotovoltaik baru, pengolahan air, transportasi dan industri lainnya.
Samtion Chemical memasok plastik teknik dan bahan khusus yang dimodifikasi dari S-Plastics dan merek lain. Produk asli kami dijamin,dengan kualifikasi lengkap dan kapasitas pasokan yang unggul dan keuntungan harga.
Setiap batch produk kami adalah subjek inspeksi kualitas yang ketat untuk memastikan pasokan asli. Semua produk memiliki sertifikat MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA!!
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lubricomp EX07305.pdf |
|