S-Plastics Lubricomp DX98306Hresin adalah
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 51 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 42 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 43 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 5.3 | % | ASTM D 638 |
| Tekanan tarik, putus | 32.8 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2060 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 5090 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 85 | MPa | ASTM D 790 |
| Modulus Flexural | 2060 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5010 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 51 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 43 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 48 | MPa | ISO 527 |
| Tekanan tarik, hasil | 5.3 | % | ISO 527 |
| Tekanan tarik, putus | 38.2 | % | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 0 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2140 | MPa | ISO 527 |
| Tekanan Fleksural | 71 | MPa | ISO 178 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Modulus Flexural | 2100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5120 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1767 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 154 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 69 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 34 | J | ASTM D 3763 |
| Dampak Multiaxial | 32 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 180 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 13 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 132 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 122 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.56E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.38E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 7.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 145 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 123 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.48 | - | ASTM D 792 |
| Kepadatan | 1.29 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.1 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 24 jam | 0.5 - 0.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.6 - 0.8 | % | ASTM D 955 |
| Penyusutan jamur, aliran, 24 jam | 0.64 | % | ISO 294 |
| Penyusutan jamur, xflow, 24 jam | 0.74 | % | ISO 294 |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 8.5 | g/10 menit | ASTM D 1238 |
| Pakai faktor pencuci | 21 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Dimodifikasi |
| COF Dinamis | 0.37 | - | ASTM D 3702 Dimodifikasi |
| COF statis | 0.32 | - | ASTM D 3702 Dimodifikasi |
| Kepadatan | 1.29 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.7 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
Pengolahan
| Parameter | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 120 | °C | |
| Waktu Pengeringan | 4 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 300 - 315 | °C | |
| Suhu depan - Zona 3 | 310 - 320 | °C | |
| Tengah - Zona 2 Suhu | 305 - 315 | °C | |
| Bagian belakang - Zona 1 Suhu | 295 - 305 | °C | |
| Suhu Cetakan | 80 - 110 | °C | |
| Tekanan Belakang | 0.2 - 0.3 | MPa | |
| Kecepatan sekrup | 30 - 60 | rpm | |
| Sumber GMD, terakhir diperbarui:09/24/2008 | |||
Dalam beberapa tahun terakhir, kami telah mengembangkan pasar domestik dan secara aktif mengeksplorasi pasar luar negeri.Hingga saat ini, kami telah menyediakan produk dan layanan berkualitas tinggi untuk lebih dari 1.000 pelanggan di berbagai industri, termasuk: elektronik dan peralatan listrik, medis, makanan,elektronik otomotif, komunikasi optoelektronik, energi fotovoltaik baru, pengolahan air, transportasi dan industri lainnya.
Samtion Chemical memasok plastik teknik dan bahan khusus yang dimodifikasi dari S-Plastics dan merek lain. Produk asli kami dijamin,dengan kualifikasi lengkap dan kapasitas pasokan yang unggul dan keuntungan harga.
Setiap batch produk kami adalah subjek inspeksi kualitas yang ketat untuk memastikan pasokan asli. Semua produk memiliki sertifikat MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA!!
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Lubricomp DX98306H.pdf |
|