SabikThermocompWX09414_BK1E523resin adalah senyawa yang didasarkan pada Thermoplastic Polyester (PBT) yang mengandung kaca.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 83 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 82 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5910 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 134 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 126 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5150 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 82 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 81 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2.3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 5650 | MPa | ISO 527 |
| Tekanan Flexural | 130 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 4960 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 688 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 101 | J/m | ASTM D 256 |
| Dampak Multiaxial | 3 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 7 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 212 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 178 | °C | ASTM D 648 |
| CTE, -30°C sampai 30°C, aliran | 5.1E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 1.22E-04 | 1/°C | ASTM D 696 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.51 | - | ASTM D 792 |
| Kepadatan | 1.5 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.06 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam (5) | 0.5 - 0.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam (5) | 0.7 - 0.9 | % | ASTM D 955 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan | 150 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 2 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 2,0 mm | 700 | °C | IEC 60695-2-13 |
| Indeks Oksigen (LOI) | 30 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:2010/08/16 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 240 - 265 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:2010/08/16 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
SS-Plastics Thermocomp WX09414_BK1E523.pdf |
|