SabikThermocompWH0270FX_WH5A289resin memiliki berat 2.7 PBT
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 0.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 0.7 | % | ASTM D 638 |
| Tekanan lentur, hasil, 2 mm/menit | 52 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 0.8 | % | ISO 178 |
| Flexural Modulus, 2 mm/menit | 8320 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 150 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 19 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 164 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 162 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 2.695 | g/cm3 | ASTM D 792 |
| Penyerapan Kelembaban, 50% RH, 24 jam | 0.08 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 24 jam | 0.69 - 0.89 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | Satu, satu.2 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui:08/13/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 240 - 265 | °C |
| Suhu depan - Zona 3 | 260 - 270 | °C |
| Tengah - Zona 2 Suhu | 245 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 230 | °C |
| Suhu Cetakan | 80 - 100 | °C |
| Tekanan Belakang | 0.2 - 0.3 | MPa |
| Kecepatan sekrup | 30 - 60 | rpm |
| Sumber GMD, terakhir diperbarui:08/13/2008 | ||