SabikThermocompEkspor dari negara lainresin adalah
resin injeksi PA66 yang dimodifikasi dampak, diperkuat serat kaca 25%.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 100 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6500 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 165 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 6000 | MPa | ISO 178 |
| Kekerasan, Rockwell L | 104 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 14 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 12 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 9 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 13 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 65 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 65 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 2.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 233 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 230 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 245 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 228 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.6 | % | Metode S-Plastics |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 5.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 2.3 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan | 500 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 400 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) | 1.6 | mm | UL 94 oleh GE |
| Glow Wire Flammability Index 650°C, melewati pada | 2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 27 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:02/11/2003 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp EXCP0123.pdf |
|