SabikThermocompR1000P112resin adalah High Impact Nylon 66 senyawa.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, pecah, 5 mm/menit | 38 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | > 300 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 650 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 22 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 99 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 40 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 2.8 - 3.2 | % | Metode S-Plastics |
| Kepadatan | 1.09 | g/cm3 | ISO 1183 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan | 3 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) | 1.6 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:05/17/2006 | |||
粘贴物性表上的表格内容 ((调整表格内容,不要出现表格行距离不一致的地方) isi tabel pada lembar stiker
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp R1000P112.pdf |
|