SabikThermocompR1000HI620resin adalah Impact modified Polyamide 66 resin injeksi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4.6 | % | ISO 527 |
| Tekanan tarik, istirahat, 50 mm/menit | > 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1900 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 72 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1900 | MPa | ISO 178 |
| Kekerasan, Rockwell R | 112 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 80 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 65 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -40°C | 55 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 80 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 65 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | > 100 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | > 100 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 192 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 190 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 72 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 65 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | Satu, satu.2 | % | Metode S-Plastics |
| Kepadatan | 1.07 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 5.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 1.5 | % | ISO 62 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+16 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+16 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 16 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.7 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.0067 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.015 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 550 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL Diakui, 94HB Kelas Api Nilai ke-2 (3) | 3 | mm | UL 94 |
| Kecepatan pembakaran FMVSS, ketebalan 2 mm | 15 | mm/menit | FMVSS 302 |
| Sumber GMD, terakhir diperbarui:11/04/2003 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 75 - 85 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.2 | % |
| Suhu Peleburan | 260 - 280 | °C |
| Suhu Nozzle | 250 - 270 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 260 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 70 - 90 | °C |
| Sumber GMD, terakhir diperbarui:11/04/2003 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp R1000HI620.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|