SabikThermocompEX06430Hresin adalahsenyawa yang didasarkan pada resin Polyetherimide yang mengandung Proprietary Filler (s).
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yield | 110 | MPa | ASTM D 638 |
| Tekanan tegangan, istirahat | 90 | MPa | ASTM D 638 |
| Tekanan tarik, hasil | 6.7 | % | ASTM D 638 |
| Tekanan tarik, putus | 13.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3660 | MPa | ASTM D 638 |
| Modulus Flexural | 3660 | MPa | ASTM D 790 |
| Tekanan tarik, yield | 106 | MPa | ISO 527 |
| Tekanan tegangan, istirahat | 90 | MPa | ISO 527 |
| Tekanan tarik, hasil | 6 | % | ISO 527 |
| Tekanan tarik, putus | 10.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3500 | MPa | ISO 527 |
| Tekanan Flexural | 133 | MPa | ISO 178 |
| Modulus Flexural | 3500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1383 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 48 | J/m | ASTM D 256 |
| Energi Dampak Instrumen @ puncak, 23°C | 10 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 73 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 195 | °C | ASTM D 648 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 194 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.34 - 1.4 | g/cm3 | ASTM D 792 |
| Penyusutan jamur, aliran, 24 jam | 0.7 | % | ASTM D 955 |
| Penyusutan jamur, xflow, 24 jam | 0.8 | % | ASTM D 955 |
| Sumber GMD, terakhir diperbarui:08/02/2007 | |||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp EX06430H.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|