SabikThermocompNoryl_RN1300resin adalah PPE bertulang kaca/mineral 15%, tidak berklorinasi, tidak berbrominasi, tahan api.
Hitam dan abu-abu.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 102 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 103 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 6.9 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3.2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 4650 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4890 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 42 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 6 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 142 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 140 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 137 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 132 | °C | ASTM D 648 |
| CTE, -40°C sampai 60°C, aliran | 3.42E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 60°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 110 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 105 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 110 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.23 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.45 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 26.6 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 4 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Diakui, Kelas Api 94V-1 (3) | 0.76 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.52 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:02/19/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 295 - 315 | °C |
| Suhu depan - Zona 3 | 280 - 315 | °C |
| Tengah - Zona 2 Suhu | 270 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 305 | °C |
| Suhu Cetakan | 75 - 105 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 30 - 70 | % |
| Sumber GMD, terakhir diperbarui:02/19/2001 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp Noryl_RN1300.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|