SabikThermocompNoryl_PO2331Bresin adalah bahan kaca/mineral yang penuh, tahan api, bebas halogen dengan dimensi yang baik
stabilitas.
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 60 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, pecah, 5 mm/menit | 75 | MPa | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 6200 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 105 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 5600 | MPa | ISO 178 |
| Kekerasan, H358/30 | 115 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 13 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 13 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 60°C, aliran | 2.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat A/50 | 125 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 115 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 120 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 95 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.2 - 0.3 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.3 - 0.7 | % | Metode S-Plastics |
| Kepadatan | 1.37 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 280°C/2,16 kg | 30 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+14 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 15 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.4 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.029 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.029 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Diakui, Kelas Api 94V-2 (3) | 0.75 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 34 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui: 18/10/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 120 | °C |
| Waktu Pengeringan | 2 - 3 | jam |
| Suhu Peleburan | 280 - 300 | °C |
| Suhu Nozzle | 260 - 280 | °C |
| Suhu depan - Zona 3 | 280 - 300 | °C |
| Tengah - Zona 2 Suhu | 260 - 280 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 260 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 80 - 120 | °C |
| Sumber GMD, terakhir diperbarui: 18/10/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp Noryl_PO2331B.pdf |
|