SabikThermocompNoryl_PCN2910resin adalah 35% Kaca / Mica diisi. modulus tinggi dan toleransi ketat cetakan untuk sasis
pasar.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 122 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 122 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 1.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.5 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/menit | 11370 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 151 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 9790 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 8750 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 106 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 106 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 1.3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 1.3 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 10600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 160 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 9130 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 331 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 58 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 7 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 14 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 4 | kJ/m2 | ISO 179/2C |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 20 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 140 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 129 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 123 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 129 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 126 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.16E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 4.68E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 129 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 65 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 65 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.38 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.1 - 0.3 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/5,0 kgf | 10 | g/10 menit | ASTM D 1238 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Diakui, Kelas Api 94V-1 (3) | 1.49 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 2.99 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 2.28 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:12/14/2001 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 295 - 315 | °C |
| Suhu Nozzle | 295 - 315 | °C |
| Suhu depan - Zona 3 | 280 - 315 | °C |
| Tengah - Zona 2 Suhu | 270 - 310 | °C |
| Bagian belakang - Zona 1 Suhu | 260 - 305 | °C |
| Suhu Cetakan | 75 - 105 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 20 - 100 | rpm |
| Menembak untuk ukuran silinder | 30 - 70 | % |
| Sumber GMD, terakhir diperbarui:12/14/2001 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Thermocomp Noryl_PCN2910.pdf |
|